DESCRIPTION
Modified amine-cured epoxy anti-static coating, specially designed for the protection of internal wall of aero oil tank and gasoline tank.
CHARACTER
Excellent protective property and stable static conductivity
Excellent resistance to oil, water and chemical reagent
Excellent adherence, hardness and weariness
Capability of cure at low temperature and high humidity
PROPERTY
Color:White gray
Gloss: Semi-gloss
Density:(20℃):1.3g/cm3 (mixed)
Non volatile content: 70%(mixed)
PACKAGING
Base: 20kg/case
Hardener: 2kg/case
APPLICATION
Surface preparing:Blast up to ISO Sa2.5 or hand tool to ISO St3. Remove oil and
grease thoroughly and keep surface clean when recoating.
Steel temperature should be above dew point 3℃ at least.
Mixing ratio: Base/hardener=10/1(by weight)
Application:
|
Application method |
Nozzle
(mm) |
Pressure (MPa) |
Thinning rate |
Dry/Wet film(um) |
Theoretical coverage(kg/m2) |
|
Brush,roller |
-- |
-- |
0-5% |
50/100 |
0.12 |
|
Air spay |
1.5-2.4 |
0.3-0.5 |
0-15% |
50/100 |
0.12 |
|
Airless spray |
0.38-0.48 |
12-15 |
0-5% |
75/150 |
0.18 | Thinner:102
Dry time(20℃):Surface drying 0.5h,Hard drying 6h
Pot life(20℃):4.5h
NOTICE
1. Practical coverage is based on the application circumstance, application method,
Surface profile, figure and area. so, take extra paint use into consideration.
2. Avoid inhalation of vapor or paint mist, as well as contact with skin and eyes.
3.Avoid painting when the temperature is below 0℃ or the humidity is over 85%
4. Paint should be stored in the dry and good ventilation circumstance which the
temperature is below 40℃.Fire is forbidden in the painting site. |